Pbl_2-PbOガラスのイオン導電率
スポンサーリンク
概要
- 論文の詳細を見る
A glassy solid electrolyte of the(1-x)PbI_2-xPbO system was prepared using two kinds of quenching methods. In the case of the iron pressing method, 0.68PbI_2-0.32PbO(x=0.32)glass was obtained when PbI_2 melt reacts with oxygen in air. In the case of the quenching method using ice water, the glassy sample was not obtained when x<0.35. Conductivity was enhanced and crystallization temperature was decreased with decreasing PbO content x. A maximum conductivity of 6.2×10^<-7> S・cm^<-1> at 373 K was obtained for x=0.32 glass plate prepared by the iron pressing method. This value is almost equal to the maximum conductivity of anion conducting glasses reported. I^- ions would be the sole carrier ions, based on an estimation of the electromotive force of the I_2 concentration cell.
- 社団法人日本セラミックス協会の論文
- 1996-03-01
著者
関連論文
- 積層型イオン導電体Li_2O・Sm_2O_3・2SiO_2+0.92ZrO_2・0.08Yb_2O_3を用いた電位検出型CO_2ガスセンサー
- ZrO2-Y2O3系固体電解質を用いた起電力法によるPb-Sn,Pb-Sb二元合金中の活量測定
- ZrO2-Y2O3系固体電解質を用いた起電力法による低温でのPb-Bi,Pb-Ag二元合金中の活量測定について
- 固体電解質を用いた起電力法による低温での各種金属酸化物の標準生成自由エネルギ-の測定
- PbX_2-PbO-SiO_2(X=Cl, Br, I)ガラスのイオン導電率
- Ag+-β′′-Al2O3固体電解質を用いたAg-Pd固体合金の熱力学的研究
- β-アルミナ固体電解質を用いたSO2ガスセンサの固体参照極について
- Pb2+-β″-アルミナを固体電解質として使用した電池によるSO2ガスセンサ-の開発
- Cu+-Ag+-β"-アルミナを固体電解質として使用した電池による SO2ガスセンサーの開発
- Pbl_2-PbOガラスのイオン導電率
- SO2ガスセンサの開発に関する基礎的研究
- PbO-SiO2融体中のPbOの活量におよぼすMgO,ZnOの影響について
- PbO-SiO2融体中のPbOの活量におよぼす鉄酸化物の影響について
- Application of Stabilized Zirconia to Electrolytic Oxidation of Pb Alloys
- 溶融鉛とPbO-SiO2融体間のCu,Asの分配について
- β″-アルミナを固体電解質としたSO2ガスセンサの現場への応用 (素材小特集-2-素材技術開発の基礎)
- 廃棄プラスチックの有効利用(各種プラスチックの熱分解-2-)
- 廃棄プラスチックの有効利用(各種プラスチックの熱分解-1-)