TiN被覆材料の残留応力に及ぼす基板表面粗さの影響
スポンサーリンク
概要
- 論文の詳細を見る
Effect of film thickness and surface roughness of substrate on the residual stress of TiN coating prepared by arc ion plating was studied. Chipping and spalling of TiN films increased with increasing surface roughness and film thickness. The thermal stress of TiN coating was calculated by finite element method(FEM)analysis. The results indicate that the thermal stress of TiN films increased with increasing surface roughness of substrates. From stress analysis by FEM and the X-ray method, it is concluded that chipping and spalling of TiN films occurrs when the total stress consisting of thermal and intrinsic stresses generated during the deposition process exceeds the mechanical strength of the TiN films.
- 社団法人日本セラミックス協会の論文
- 1995-02-01
著者
関連論文
- 放射光を用いたXPSおよびXASによるCrN表面酸化過程の検討
- プラズマCVD法による TiN 膜形成過程における活性プラズマ種
- ア-クイオンプレ-ティング法により作製したTiN,CrNおよびTiAlN膜の高温酸化特性 (素材小特集-4-界面反応と材料特性)
- セラミックコ-ティング膜の密着力の評価 (素材小特集-1-界面反応)
- 気相膜の特性と応力
- 「分かり易い耐火物の反応」 固体-固体
- TiN被覆材料の残留応力に及ぼす基板表面粗さの影響
- ハードコーティング材料の硬さ,密着力,応力
- TiN, (Ti, Al) N, CrN膜の高温酸化
- アークイオンプレーティング膜の特性と工業的応用
- マルチア-ク法イオンプレ-ティングによるハ-ドコ-ティング (素材部門特集号)
- イオンプレ-ティングによる窒化物膜 (セラミックスへのプラズマ利用)
- アークイオンプレーティング法によって形成した窒化物膜の高度と密着力