負荷漸増試験による高靭性窒化ケイ素の疲労強度及び損傷の評価
スポンサーリンク
概要
- 論文の詳細を見る
In order to evaluate statistical characteristics of both static and cyclic fatigue strength in HIP and normal sintered silicon nitrides, namely toughened Si_3N_4 and SN1, load, P-increasing(quasi-static loading)test and load range, ΔP-increasing(cyclic loading)test were conducted in the room air. Acoustic emission(AE)method was attempted during the fatigue tests for the toughened Si_3N_4. The SN1 exhibited static fatigue behavior, while the static strength of the toughened Si_3N_4 was independent of time, i. e., no static fatigue. However, cyclic fatigue behavior appeared in the both materials. ΔP-increasing tests with different initial value of maxmum stress, σ_<max, i> enabled to evaluate cyclic loading condition under which fatigue damage nucleated. The result suggested that σ_<max, i> influenced on the maximum stress at failure, σ_<max, f> for statistically weak specimens in the both materials, and thus fatigue damage was nucleated at lower stress levels for these specimens. Although this behavior could not be confirmed by AE analysis, AE waveform simulation revealed that the crack volume nucleated under the cyclic loading were smaller than those under quasi-static loading. Based on the above results, observation of fracture surfaces and finite element analysis, the fracture mechanisms of static and cyclic fatigue were discussed in detail.
- 2000-09-01
論文 | ランダム
- 肝疾患における細胞性免疫の研究--血清中HBs抗原の有無とT cell,B cell分布を中心に
- ベクトルポテンシャル凝縮節点空間回路網による種々のフォトニック結晶媒質条件における伝送特性の解析
- 線引き課題における筆記用具の把持形態と操作性 : 幼児期おける発達的特性について
- 明治期の横浜公園芝生事情 : 緑の毛氈と呼ばれたYC & ACクリケット・グラウンド
- 国際会計基準委員会の再出発 (甲南大学経営学部開設40周年記念論集)