The behavior of SOEC was investigated as compared with that of solid oxide fuel cell (SOFC) using small cells prepared on ytrria stabilized zirconia (YSZ) planar discs. Ni-YSZ cermet negative electrode showed asymmetric behavior indicating the existence of diffusion limited process in the electrolysis direction, although the behavior was strongly dependent on the electrode preparation. The behavior of positive electrodes made by using perovskite type oxides was also investigated. When polarized anodically, the positive electrode showed degradation behavior which ended up with electrode delamination from electrolyte. The degradation rate was remarkably decreased by improving the initial polarization performance of the electrode or by using a mixed ceria intermediate layer between YSZ and electrode. Polarization measurements of SOEC were conducted at 1173 K, 1223 K and 1273 K with various water content in hydrogen simulating the atmosphere of various water electrolysis rate. The cell was shown to work at a high current density and at high water electrolysis rate without suffering from diffusion lumiting current.
- 社団法人日本セラミックス協会の論文
- 1997-05-01
著者
-
永田 進
電総研
-
嘉藤 徹
電総研
-
嘉藤 徹
電子技術総合研究所エネルギー基礎部
-
永田 進
電子技術総合研究所エネルギー基礎部
-
加賀 保男
電子技術総合研究所
-
門馬 昭彦
電子技術総合研究所エネルギー基礎部エネルギー材料研究室
-
門馬 昭彦
電子技術総合研究所
関連論文
- 高調波測定による固体電解質電極反応のメカニズムの研究
- 平板型固体酸化物セルによる高温水蒸気電解システムの電気分解効率
- 2506 小型コージェネ用低温動作 SOFC と PEFC システム出力特性比較
- 円筒型固体電解質燃料電池の残留応力解析
- 円筒型高温水蒸気電解セルの温度分布予測
- MHD燃焼ガスの温度およびカリウム濃度の測定に関する研究
- MHD燃焼ガスの温度およびカリウム濃度の測定に関する研究
- D106 平板型固体酸化物燃料電池とガスタービン複合発電のサイクル計算
- β"アルミナ固体電解質を用いた熱電発電とヒートポンプのサイクル解析
- 円筒直列接続型固体電解質燃料電池の接合法とガスシ-ル構造
- 固体電解質燃料電池用合金系基体管の製作技術と特性評価
- 金属構成要素を用いた新円筒型固体電解質燃料電池
- 円筒型固体電解質燃料電池用合金系インタ-コネクタ膜の開発(1)
- 金属構成要素を用いた新円筒型固体電解質燃料電池の出力安定化と耐久性能評価
- 〔工業技術院電子技術総合研究所〕研究設備紹介-11-超音波顕微鏡の応用--セラミックス内部の非破壊探査
- MHD 発電用 BeO セラミック絶縁壁に関する実験的研究
- 固体電解質による高温水蒸気電解セルの分極特性
- 発電用電極材料 (溶射技術) -- (機能性材料への応用)