窒化アルミニウム添加エポキシ樹脂の熱伝導率
スポンサーリンク
概要
- 論文の詳細を見る
The thermal conductivity of an AlN- and an alumina-particulate-filled epoxy resin was investigated as a function of their volume content ratios. AlN composite exhibited thermal conductivity of 7.15 W/m・K at 68.5 vol% filler content but that of alumina composite was lower than 2.68 W/m・K even if the filler content was as much as 63.8 vol%. The thermal conductivity of the composites is strongly dependent on that of the filler. In the AlN filler properties, the particle size of the filler used affected the thermal conductivity of composites, and composites with higher thermal conductivity could be obtained by using filler with large particle size. The thermal conductivity of composites is governed by the number of resin layers on the surface of an AlN particle. The composite thermal conductivities decreased with increasing the oxygen content of the filler. The thermal conductivity of AlN particle depends on the oxygen content of the particle itself and the decrease of the composite thermal conductivity with the increase of the oxygen content of the filler is due to the increase of the aluminum oxide layer thickness produced on the surface of particles. In the thermal conductivity model, the measured thermal conductivity of AlN-ground-powder-filled composites disagreed with the ones calculated using Bruggeman's expression. However the measured values of alumina-spherical-powder-filled composites agreed with the calculated ones. It is considered that the results depended on the sphericity of the used powder.
- 1997-03-01
著者
関連論文
- 1B10 AlN 粉体の構造と化学的安定性 (2)
- 1B09 AlN 粉体の構造と化学的安定性 (1)
- 窒化アルミニウム添加エポキシ樹脂の熱伝導率
- Y_2O_3助剤での窒化アルミニウムの焼結に及ぼす酸素量の影響
- ゾル-ゲル法によるアルミニウム箔上へのNb_2O_5薄膜の作製と容量特性
- 遷移金属酸化物を添加した遮光性窒化アルミニウムの合成と特性
- 湿式粉砕によるAlN微粉末の作製と特性評価
- AlNの焼結挙動に及ぼす粉体特性の影響 (特集 材料の高純化のための微量元素の分析と解析)
- 球状窒化アルミニウムフィラーの開発
- シリコンオキサイドで被覆された研磨窒化アルミニウム基板
- シリコンオキサイド薄膜による窒化アルミニウム基板表面の平坦化