• ESR studies of radiophotoluminescence (RPL) centers in silver-activated phosphate glass were performed after the glasses had been γ-irradiated at 77°K. It is shown that the silver ions act as traps for both electrons and positive holes. By the separate formation of electron-trapped silver centers and hole-trapped silver center, it was verified that all these silver centers act as RPL centers. It was found that a positive hole in PO_4 tetrahedron is transfered to Ag^+ ion and this process is the main reason of RPL build-up. Stabilization phenomenon of RPL centers was found. It was found that alkali and or silver ion migration is necessary for stabilization. The reason why RPL in these glasses has high stability and builds-up after γ-irradiation was clarified. The resonances which are considered due to exchange coupled pairs, triads and higher aggregates of electron-trapped silver centers were found.

• 社団法人日本物理学会の論文
• 1967-11-05

著者

• Yokota Ryosuke

  Central Research Laboratory Tokyo Shibaura Electric Co. Ltd.

• Imagawa Hiroshi

  Central Research Laboratory Tokyo Shibaura Electric Co. Ltd.

関連論文

• Off-Axial Modes in Cylindrical Glass Laser Rods
• Radiophotoluminescent Centers in Silver-Activated Phosphate Glass
• Eu^ Ion as Electron Trap in Glass
• ESR Studies of Radiophotoluminescent Centers in Silver-Activated Phosphate Glass
• Lithium-7 Dosimeter Glass for Simultaneous Measurement of Thermal Neutron and Coexisting γ-ray Dose
• Some Improvements on Spherical Capsule Type Glass Dosimeter

スポンサーリンク