Absorption of Carbon Mono-Oxide by the Barium Getter Part IV. Absorption Experiments in, the Temperature Range between 0℃ and 250℃
スポンサーリンク
概要
- 論文の詳細を見る
The absorption properties of the flashed barium getter beyond 0℃ were studied. At low temperatures, carbon mono-oxide was apparently absorbed by the getter, while its resistance remained almost unvaried. At higher temperature than about 150℃, however, the resistance changed remarkably as the getter absorbed the gas. The ionization of the introduced gas made the absorption of the getter slightly vigorous. In the c.f. method the pressure decreased at first to a minimum value and then it began to increase, suggesting that another kind of gas was formed by the catalytic action on the getter surface. The phenomena were studied in details. The alternative introduction of carbon mono-oxide and oxygen gave a clue to the absorption state of carbon mono-oxide.
- 社団法人日本物理学会の論文
- 1952-08-25
著者
-
ARIZUMI Tetsuya
Kobe Kogyo Corp
-
KOTANI Seiichi
Kobe Kogyo Corporation
-
Kotani Seiichi
Kobe Kogyo Corp.
-
Arizumi Tetsuya
Kobe Kogyo Co.
関連論文
- Absorption of Nitrogen by Evaporated Film of Barium.
- On the Activation of the Oxide Coated Cathode.
- Absorption of Carbon Mono-Oxide by the Barium Getter Part IV. Absorption Experiments in, the Temperature Range between 0℃ and 250℃
- Absorption of Carbon Mono-oxide by the Barium Getter Part III. Lattice Imperfections
- Absorption of Carbon Mono-oxide by the Barium Getter Part I. Experiments at Low Temperatures
- Absorption of Carbon Mono-oxide by the Barium Getter Part II. Theory of Physical Adsorption
- Gettering Process of Barium : Sorption Properties of Oxygen to Barium
- On the Thoria Coated Cathode.
- Absorption of Carbon Mono-Oxide by the Barium Getter Part V. Theory of Absorption
- Conductivity and Electronic Energy State of Thoria Coated Cathode.
- On the Schottky Effect of the Oxide Coated Cathode
- On the Secondary Electron Emission from the Thoria Coated Cathode and the Thin Film Deposited by Evaporation from the Cathode.
- On the Electrical Conductivity of Alumina.
- The Evolution of Gas from Nickel Plate