Electron Diffraction Study of Evaporated Face-centered Cubic Crystallites

スポンサーリンク

概要

• 論文の詳細を見る

• Germer and White (Phys. Rev. 60 (1941) 447) found that thin evaporated films of face-centered cubic metals produce electron diffraction patterns with anomalous intensities. Kimoto (J. Phys. Soc. Japan 8 (1953) 762) studied the anomaly by a trial method and attributed it to stacking faults in crystaliites. By the radial distribution analysis the present author confirmed Kimoto's conclusion. Intensities of diffraction patterns from evaporated silver were accurately measured by the sector-microphotometer method and they were turned into radial distribution function. These functions reveal anomalous peaks caused by stacking faults. After a specimen is annealed at 350℃ for 3.5hrs., although crystallites do not grow remarkably, these peaks disappear. The amplitude of thermal vibration is found to be 0.15±0.02Å which agrees well with that for massive silver crystal. The narrowing of the first neighbor peak is found and is attributed to the correlative thermal vibration. Gold shows the same anomaly as is observed for silver, but aluminum shows no anomaly. These facts are in accordance with the value of stacking-fault energy.

• 社団法人日本物理学会の論文
• 1958-09-05

著者

• Morimoto Hidetake

  Physical Institute Nagoya University

関連論文

• Electron Diffraction Study of Evaporated Films of Nickel and Cobalt
• Electron Diffraction Study of Evaporated Face-centered Cubic Crystallites

スポンサーリンク