白銑の凝固速度について
スポンサーリンク
概要
- 論文の詳細を見る
The solidification rate of white cast iron and the effect of casting temperature, mould temperature and casting size upon it were studied by means of the "pour-out method". By investigation of the roughness and microstructure in the solidification-front surface, the mechanism of solidification was discussed. The results obtained were summarized as follows : - (1) In the solidification of white cast iron, the linear relation between the thickness of solidified layer and the square root of solidification time was satisfied only in the early stage of solidification and it deviated from the above relation as time proceeded. Then, the solidification curve was the form of S letter which had two points of inflexion, in other words, white cast iron was solidified through three stages. (2) From the linear relation in the early stage, the following equation, what was called an "equation of rate of skin formation" could be derived, d=k√<t>-a. where, d : solidified layer (in inch) t : solidification time (in mn) k : solidification constant a : constant k or "rate of skin formation" decreased as the casting temperature and mould temperature became higher and the casting size became larger. (3) As solidification proceeded, the roughness in solidification-front surface became larger according to its solidification curve. And it becames larger with increase of the casting temperature, mould temperature and casting size. (4) The first point of inflexion in solidification curve was the beginning point of crystallization of a "bee-hive" like ledeburite and the second one was the end point of crystallization of dendritic cementite. With increase of the casting temperature, mould temperature and casting size, these points. became later and their time interval became longer, and consequently the microstructure became rough. (5) From the results above mentioned, the schematic diagram of solidification of white cast iron was drawn and the reason for the appearance of two points of inflexion was explained.
- 社団法人日本鉄鋼協会の論文
- 1956-04-01
著者
関連論文
- 鋼のオーステナイト結晶粒度と機械的性質について
- 65 二, 三の鋼の電解研磨面と機械研磨面とのミクロ・ビツカース硬度差について(加工・性質, 第 57 回講演大会講演大要)
- 防音車輪
- 球状黒鉛鋼ロールの研究
- 152 球状黒鉛鋼ロールの研究(性質, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 混粒に関する研究 (II) : 混粒の発生原因について(その 2)
- 混粒に関する研究 (II) : 混粒の発生原因について(その 1)
- 89 鋼の一次組織に関する研究 (II) : 一次組織と偏析の関係について(鉄鋼の加工および性質, 第 55 回講演大会講演大要)
- 混粒に関する研究 (I) : 鋼質におよぼす混粒の影響について(その 2)
- 東海鋼業若松工場(第 54 回講演大会工場見学記)
- 九州造船(第 54 回講演大会工場見学記)
- 日立金属若松工場(第 54 回講演大会工場見学記)
- 混粒に関する研究 (I) : 鋼質におよぼす混粒の影響について(その 1)
- オーステナイト結晶粒の成長性におよぼす高温加工の影響について
- 57 混粒に関する研究 (III) : 偏析と混粒の関係について(第 54 回講演大会講演大要)
- 85 鋼の一次組織に関する研究 (I) : 脱酸条件と一次組織の関係について(第 53 回講演大会講演大要)
- 43 オーステナイト結晶粒の成長速度について(第 52 回講演大会講演大要)
- 粗粒鋼におけるオーステナイト結晶粒の成長性に関する二, 三の知見
- 白銑の凝固速度について
- 47 オーステナイト結晶粒の成長特性に及ぼす高温加工の影響について(第 51 回講演大会講演大要)
- 10 混粒に関する研究 (II) : 混粒の発生機構について(第 51 回講演大会講演大要)
- 9 混粒に関する研究 (I) : 鋼質に及ぼす混粒の影響について(第 51 回講演大会講演大要)
- オーステナイト結晶粒の成長性に關する二, 三の観察
- 55 Cr-Mo 強靱鋼の低温燒戻状態における衝撃遷移特性に及ぼす Al Ti 及び B の影響(日本鐵鋼協會第 48 回講演大會講演大要)
- 53 粗粒鋼におけるオーステナイト結晶粒の成長性に關する二三の知見(日本鐵鋼協會第 48 回講演大會講演大要)
- 39 オーステナイト結晶粒の成長性に關する二, 三の觀察(日本鐵鋼協會第 47 囘講演大會講演大要)
- 108 白銑の凝固速度に就いて(日本鐵鋼協會第 45 回講演大會講演大要)
- 101 粒状黒鉛鑄鐵の顯微鏡組織と疲勞強度との關係に就いて(日本鐵鋼協會第 44 回講演大會講演大要)
- Cr-Mo 強靭鋼の低温燒戻状態における衝撃遷移特性に及ぼす Al, Ti 及び B 添加の影響