CeF_3 沈殿分離-炎光分析法による低水素系溶接棒被覆剤ならびに同原料中の F の間接定量
スポンサーリンク
概要
- 論文の詳細を見る
An indirect determination of F by flame emission spectrometry was studied. After a sample was fused with Na_2CO_3, F was precipitated as CeF_3, and Ce in CeF_3 which was separated by filtering was determined by flame emission spectrometry in a nitrous oxide-acetylene flame. The intensity of Ce in the concentration range of 0 to 1200 ppm was measured at 520nm, and was increased by adding Sr. When the minimum of CH_3COONH_4 which was necessary to precipitate CeF_3 rapidly was added to the solution, co-precipitated cerous acetate could be dissolved by washing with NH_4NO_3 solution when filtering the precipitate. The recovery of 5mg or over F was 98-102%. This method was successfully applied to the determination of F in the coating of the low hydrogen type of electrode, fluorides of alkaline earth metals, and cryolite. The reproducibility (coefficient of variation) of the results was 1.46-3.48%.
- 社団法人日本鉄鋼協会の論文
- 1976-07-01
著者
関連論文
- 309 裏波溶接用塗布式フラックスに関する研究
- 423 SCM440とSUS304の継手部における炭素移行について
- 459 WWW対応の溶接データベースシステム開発(4) : ニッケル合金ワイヤを用いた異材溶接事例
- 451 溶接データベースシステムの開発(3) : 複式アーク溶接の特性評価と加工事例データベース化
- 19Cr-9Ni ステンレス鋼溶着金属中の酸化介在物について
- 軟鋼溶着金属中の酸化介在物について
- CeF_3 沈殿分離-炎光分析法による低水素系溶接棒被覆剤ならびに同原料中の F の間接定量
- CaF_2 沈殿分離-原子吸光分析による低水素用溶接棒被覆剤ならびに同原料中の F の間接定量
- 原子吸光分析による軟鋼用溶接棒被覆剤中の各成分の定量
- HT-80 鋼のサブマージドアーク溶接に関する研究
- 27aXA-7 Cooper Pairsの熱的安定化機構(高温超伝導理論・低次元系理論)(領域8)
- 28pSL-7 Cooper pairの熱的安定化による原子核の安定化
- 29a-B-2 超伝導相転移の前駆状態を形成する高温磁気相転移