固態滲炭劑に就て
スポンサーリンク
概要
- 論文の詳細を見る
The present work shows the result of research regarding the solid carburisers as follows, 1. Composition and volume of evolving gas from solid carburisers when heated up to high temperature. 2. Comparison between carburising powers of various solid carburisers. The author has reached the following conclusion, 1. The evolving gases from solid carburisers contain a large quantity of Hydrogen and hydro carbon at primary heating, but they are replaced by carbon-oxygen gases at secondary and afterward heating. 2. Ratio between CO to CO_2 and H_2 to CH_4 gases, evolved at high temperature, agrees with the equilibrium systems of Boudouard Rhead and Wheeler, and Schenk. 3. Carbonate as energisers, accelerates the carburised action at such a low temperature as it does not decompose, but de composed carbonate can not accelerate so strongly as undecomposed carbonate. Then, carburiser mixed with carbonate, decomposed temperature of which is very high, does not decrease rapidly the carbuising power after repeated cabrurisations. 4. The carburisation mechanism of the solid carburiser must agree with the theory of CO-CO_2 Fe, hut it must be in more powerful condition on account of the presence of great many quantity of solid carbon.
- 社団法人日本鉄鋼協会の論文
- 1928-04-25
著者
関連論文
- 窒素硬化に及ぼす Al, Cr, Mn, Ni の影響(日本鐵鋼協會第拾壹囘講演大會)
- 11) 窒素硬化に及ぼす Al, Cr, Mn, Ni の影響(日本鐵鋼協會第拾壹囘講演大會)
- 窒素硬化に及ぼす Al, Cr, Mn, Ni の影響
- 窒素硬化鋼に就て
- 窒素硬化用鋼の炭素量の窒素硬化に及ぼす影響
- 固態滲炭劑の滲炭力減衰に就て
- 固態滲炭劑に就て
- 9) 固態滲炭劑に就て(日本鐵鋼協會第三囘講演大會)