酸化チタンのカルシウム熱還元法による粉末チタンの製造

概要

論文の詳細を見る
According to the measurements of equilibrium oxygen concentration in Ti under Ca-CaO co-existence, the deoxidation limit is 500 ppm at 1273K. On the basis of these data, preparation of Ti powders have been carried out by reduction of TiO_2 using saturated Ca vapors, liquid Ca and CaH_2 powders at 1273K and subsequent rinsing of CaO in the aqueous solution of HCl, CH_3COOH or NH_4Cl. The oxygen and calcium levels in the Ti powders reduced by the saturated Ca vapors and the liquid Ca were not below 2000 and 1000 ppm, respectively. This was attributed to the CaO which were confined inside the sintered Ti particles and could not be exposed to the rinsing solution. Reduction of the TiO_2-CaO mixtures has led to the residual oxygen with the range of 1000-2000 ppm, thus the presence of CaO in the starting oxide was effective to control the sintering between reduced Ti powders. The particle size of the reduced Ti was 1-10μm. Reduction of TiO_2 by mixing with excess amount of CaH_2 powders could eliminate oxygen below 700 ppm which is close to the deoxidation limit for Ti by Ca of activity of unity.
社団法人日本鉄鋼協会の論文
1990-04-01