Si, N によるオーステナイトステンレス鋼の高温強度の改善(高温の組織と強度)(<特集>耐熱鋼・耐熱合金)

概要

論文の詳細を見る
The effect of additions of Si, N and C on the creep rupture strength of Ni-Cr austenitic steel was studied, and the effect of heat treatment on the creep strength of 2%Si-13%Ni-24%Cr-0.25%N steel was also studied. The creep rupture strength at 1000℃ depends on Si/N and the maximum value is obtained at Si/N≈10. Strengthening by additions of Si and N may be attributed mainly to the retardation of the Cr-nitride precipitation by addition of Si. Rupture elongation increases with Si content. Creep rupture strength at 1000℃ increases with C content up to 0.10%, above which the strength decreases at longer time. Based on these data, 0.1%C-2%Si-13%Ni-24%Cr-0.25%N austenitic steel is designed for radiant tube use. In this steel further improvement of the strength is obtained by high temperature (1200∿1250℃) solution treatment. In this condition, the creep rupture strength of this steel is included in the data band of HK40 surveyed by Nishino. The creep rupture strength at 1000℃ decreases with ageing or cold working. Welded tube of this steel is put to the test for radiant tube, and it was found that this steel has excellent performance and durability.
社団法人日本鉄鋼協会の論文
1979-06-01