低炭素鋼の低温脆性破面と組織の関連性
スポンサーリンク
概要
- 論文の詳細を見る
The brittle fracture surfaces of the ferrite-pearlite and the martensite structure in low carbon steels were investigated with a scanning electron microscope. The direct correspondence between the fracture surface and the microstructure was made, and the dependence of the fracture mode on grain size was studied from the view point of the crystallographic orientatio relationship. The fracture surface prepared by the Charpy impact test revealed the discontinous fracture process ; it consisted of the repetition of nucleation and propagation of the microcrack, and the cleavage plane was determined as {100} by the orientation measurements of the facet pit and the fracture surface. These microcrack propagation units could be considered as the fracture facets and those in ferrite-pearlite structure were composed of some adjacent grains in which the crystallographic orientation differences about fracture surface {100} were very small. The fracture facet was generally larger than the ferrite grain size, but it did not correspond to the austenite grain directly. The martensite structure, both as quenched and tempered, had the domains in which the crystallographic orientation of laths was uniform and the crack also nucleated and propagated in {100}.
- 1972-02-01
論文 | ランダム
- 肝門部胆管癌と鑑別が困難であった原発性硬化性胆管炎の1例
- 残胃壁内転移で再発したCY1胃癌の一切除例
- PP-1-266 肝細胞癌に対する鏡視下手術の現状
- 鏡視下肝切除術の現状と問題点
- 癌手術後のShort Bowel Syndromeに対するH_2受容体拮抗剤の臨床的意義