電炉処理ダスト中亜鉛化合物の形態別定量(湿式化学分析)(<特集>最先端の化学分析と物理解析)
スポンサーリンク
概要
- 論文の詳細を見る
The analytical methods for Zn compounds in the dust recovered from the electric furnace dust have been investigated. The recovered dust contains metallic Zn, ZnO, ZnS and trace amount of Zn(OH)_2 as Zn compounds. The sample was dissolved in the FeCl_3-citric acid solution at room temperature. During the dissolution, metallic Zn reduced Fe(III) to Fe(II) quantitatively. The amount of Fe(II) was determined by the titration with potassium dichromate, and converted to the amount of metallic Zn. The ZnS contained in the residue was dissolved in HNO_3(1+1), and the amount of Zn as ZnS was determined by ICP-AES. The amount of ZnO and Zn(OH)_2 was obtained by subtracting the amounts of metallic Zn and ZnS from the amount of total Zn. The electric furnace dust contained ZnO and ZnFe_2O_4, and the FeCl_3-citric acid solution was used for the separation of ZnO from ZnFe_2O_4. Only ZnO was dissolved in the FeCl_3-citric acid solution, and ZnFe_2O_4 contained in the residue was determined by ICP-AES after alkali fusion and acid dissolution.
- 社団法人日本鉄鋼協会の論文
- 1999-02-01
著者
-
吉岡 啓一
川崎製鉄(株)技術研究所
-
吉岡 啓一
川鉄鉱業(株)
-
志村 眞
川崎製鉄(株)技術研究所
-
藤本 京子
川崎製鉄(株)技術研究所
-
志村 眞
JFEスチール(株)スチール研究所
-
志村 眞
川崎製鉄 技研
-
藤本 京子
Jfeスチール(株)スチール研究所
-
吉岡 啓一
川崎製鉄株式会社 技術研究所
-
志村 眞
川崎製鉄(株)分析・物性研究センター
関連論文
- 554 共金系ワイヤで溶接した SUS444 の TIG 溶接部の継手性能(ロール摩耗・圧延油・熱処理・ステンレス鋼・溶接, 加工, 日本鉄鋼協会第 104 回(秋季)講演大会)
- FIBを用いたTEMによるすずめっき鋼板の断面組織観察
- 二次イオン質量分析法による鉄-20クロム-5アルミニウム合金の高温酸化皮膜の分析(質量分析法の応用技術)
- 18 mass%Cr鋼における粒界析出物およびCr欠乏層のTEM観察
- Fe-20mass%Cr-5mass%Al合金に生成したアルミナ皮膜でのLaおよびZrの粒界偏析
- 鉄鋼中微量酸素定量における前処理法の開発
- 高耐酸化性20%Cr-5%Al-La-Zr鋼「R20-5USR」の開発 (ステンレス鋼)
- 建材用Zn系めっき鋼板のロールフォーミング加工性の改善
- 発光分光分析と極値統計を用いた鋼中酸化物の粒径分布,最大粒径および組成の分析技術開発
- Fe-Cr-Al合金に生成したアルミナ皮膜での粒界偏析