鋼種による熱応力亀裂の発生度合を比較するための高温弾性率および熱膨脹率の測定 : 鋼塊の熱応力亀裂に関する研究 III
スポンサーリンク
概要
- 論文の詳細を見る
According to the kinds of steels there are some differences in the frequency of thermal stress crackings which occur in the heating process of ingots. In this report, we measured Young's modulus and the coefficient of thermal expansion of typical steels, within the temperature range of room tempereature to 1000℃, because they influence the thermal stress. And using the results we compared the rate of frequency of thermal stress crackings according to the kinds of steels. The results obtained are as follows : (1) It was found that the Young's modulus decreases rectilinearly up to 400℃ and curvilinearly over about 500℃ to 600℃ in all the steels tested. And the modulus is not influenced greatly by a small change of the components, the inclusions heat treatment, etc. of steels, but there is some difference among the kinds of steels classified roughly. (2) As for the coefficient of thermal expansion there is little difference with a small change in heat treatment for the same kind of steels but a considerably large difference according to the components of steels. This influence of the components is not very great under the transformation point but it becomes very great above the point (i. e. Austenite range). Especially when carbon content increases, the coefficient of thermal expansion increases heavily. (3) To estimate the magnitude of thermal stress which occurs when steels complete the transformation we utilized Young's modulus and coefficient of thermal expansion, and found that thermal stress increases chiefly in accordance with the increase of carbon content. It follows from this that thermal stress is greatest in hyper-eutectoid steel of JIS SK2, SUJ 2, 3. Consequently we can conclude that thermal stress crackings are most liable to occur in these kinds of high-carbon steel.
- 社団法人日本鉄鋼協会の論文
- 1963-12-01
著者
関連論文
- 高炭素鋼鋼塊の加熱過程における内部亀裂の発生について : 鋼塊の熱応力亀裂に関する研究 IV
- 160 鋼中に生成するチタン炭化物, 窒化物ならびに炭窒化物について(性質, 日本鉄鋼協会第 68 回(秋季)講演大会講演論文集 (II))
- 135 快削軸受鋼の研究(耐候性鋼・快削鋼, 加工・性質・分析, 日本鉄鋼協会 第 81 回(春季)講演大会)
- 197 快削軸受鋼について(鋳鋼・鋳鉄・被削性・疲労・その他, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 582 極低鉛快削肌焼鋼の被削性(快削鋼, 材料, 日本鉄鋼協会第 113 回(春季)講演大会)
- 鋼中に生成する硫化物系非金属介在物の挙動について
- 鋼種による熱応力亀裂の発生度合を比較するための高温弾性率および熱膨脹率の測定 : 鋼塊の熱応力亀裂に関する研究 III
- 鋼塊の加熱過程における熱応力について : 鋼塊の熱応力亀裂に関する研究 II
- 加熱過程における鋼塊内部の温度分布について : 鋼塊の熱応力亀裂に関する研究 I
- 110 加熱過程における内部亀裂の生因について : 鋼塊の熱応力亀裂に関する研究 II(加工, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)
- 109 鋼塊における熱応力の理論的解法について : 鋼塊の熱応力亀裂に関する研究 I(加工, 日本鉄鋼協会第 64 回(秋季)講演大会講演大要)