鐵及び鐵合金の高温酸化に關する研究 (VII) : Fe-Al, Fe-Cr-Al, Fe-Si 各合金の酸化物被覆について

スポンサーリンク

概要

• 論文の詳細を見る

• The structure of the scale of the Fe-Al, Fe-Cr-Al and Fe-Si alloys was observed. The relation between the thickness of each layer of the scale and aluminium content when the Fe-Al alloys were heated in the air at 1200℃ for 1 hour, were shown in fig. 1. The chemical compositions of the I, II, III and IV layer were Fe_2O_3, Fe_3O_4, FeO and FeO・(Fe, Al)_2O_3, respectively. The Fe-Al alloys produced α-Al_2O_3 film on their surface. On the Fe-Cr-Al alloys which contained comparatively small content of aluminium and Chromium, the three layered scale which was consisted of Fe_2O_3, Fe_3O_4 and FeO・(Fe, Cr, Al)_2O_3, was produced. The thickness of the scale of the Fe-Si alloys was shown in fig.6 with reference to silicon content. The scale of the Fe-Si alloys lower than about 3% Si, was consisted of four layers Fe_2O_3, Fe_3O_4, FeO and Fe_2SiO_4 one. On the surface of the high silicon alloys, SiO_2 (β-tridymite) film was produced.

• 社団法人日本鉄鋼協会の論文
• 1950-07-25

著者

• 三島 徳七

  東京大學第一工學部冶金學教室

• 椙山 正孝

  東京大學第一工學部

関連論文

• 耐久磁石合金の研究 (IV) : 各種磁石鋼の時効硬化機構に就いて
• 耐久磁石合金の研究 (II) : 冷間加工せる高 Mn 鋼の磁性に就いて
• 鐵及び鐵合金の高温酸化に關する研究 (VIII) : アルミニウム熔射による鐵鋼の高温酸化防止について
• 鐵及び鐵合金の高温酸化に關する研究 (VII) : Fe-Al, Fe-Cr-Al, Fe-Si 各合金の酸化物被覆について
• 鐵及び鐵合金の高温酸化に關する研究 (VI) : Fe-Cr 合金の酸化物被覆の構造
• 鐵及び鐵合金の高温酸化に關する研究 (V) : 耐酸化限界温度について
• 鐵鋼中に於けるジルコニウム
• Cr 鋼滲炭層の特性とその熱處理による改善
• 特殊鋼のオーステナイト粒子生長の特性 (II)

スポンサーリンク