ベリリウム銅合金板における析出硬化
スポンサーリンク
概要
- 論文の詳細を見る
Beryllium-copper and beryllium-tin-copper alloy sheets were solution treated at 800℃ or 820℃ and quenched in water or oil, and then annealed at temperature below the recrystallization temperature. The bending plasticity and Vickers hardness of these samples were measured as functions of annealing temperature. On the curves plotting Vickers hardness versus the annealing temperature a small maximum at about 160℃ (annealing time was one hour in each case) was found. It is highly improbable that this hardening is due to any impurity and it is probable that this hardening occurs prior to two-dimensional and three-dimensional precipitations. (Received December 11, 1952)
- 宇宙航空研究開発機構の論文
- 1953-02-28
著者
関連論文
- 稀土元素の超微細構造成分の強度の表
- As IIのスペクトルの4s4p^3のタームの超微細構造
- 1-23.He IIのスペクトルのレベル・シフト(理工學研究所第5囘定期講演會講演アブストラクト)
- No.32 Sb II, Sb III及びBi IIのスペクトルについて(第2報)
- SbII,SbIII及びBiIIスペクトルについて(第1報)
- SbII,SbIII及びBiIIスペクトルについて(第1報)
- 原子核のモーメントの表
- 黄銅の圧延板における低温燒鈍効果
- ベリリウム銅合金板における析出硬化
- 1-19.冷間圧延をした純銅及びりん青銅の板に対する低温燒鈍の影響(金属材料,金属物理)(第九囘定期講演會講演要旨)
- 2-65.不誘鋼の發條について(東京大学理工学研究所第6回定期講演會プログラム)
- 2-10.燐青銅の壓延板に於ける燐の役目(理工學研究所第5囘定期講演會講演アブストラクト)
- 可削性黄銅板(時計齒車用黄銅板)(金屬學)
- 1-20.可削性黄銅板(理士學研究所第4囘定期講演會講演アブストラクト)
- 炭素鋼バネ(時計用ゼンマイ)(金屬學)
- 黄銅,洋白,マンガン黄銅の壓延板のたわみの塑性(第2報)(金屬學)
- 2-7.冷間加工したニッケルの再結晶について(理工學研究所第3回定期講演會講演アブストラクト)
- 黄銅,洋白,マンガン黄銅の壓延板のたわみの塑性(第1報)(金屬學)
- 冷間加工したニッケルの再結晶(物理學)
- 金屬壓延板の硬度(物理學)
- No.46薄い板のたわみの彈性と銅合金における析出現象(第4報) : ベリリウム銅合金の板
- 薄い板のたわみの彈性と銅合金における折出(第3報)現象りん青銅の壓延板
- 圧延した低錫りん青銅板のたわみの塑性
- 金屬の薄い板のたわみの彈性と銅合金における折出硬化(第2報)
- 金屬の薄い板のたわみの彈性と銅合金における折出硬化(第1報)