鋳鉄の成長について
スポンサーリンク
概要
- 論文の詳細を見る
The degree of growth of several kinds of cast iron, when they were hested in vacuum, was observed with dilatometer. When they were heated at a constant temperature, 7CO℃, a little below Ai transformation point, their growth was nearly proportional to the growth of the graphite in them. But when they were heated repeatedly between 600℃ and 900℃, their growth was not proportional to that of the graphite in them, and also much larger than that caused by the graphiti zation. This additional growth seemed to depend on the cracks which were generated in graphite. Chromium bearing cast iron grew up a little during the first heating cycle, but gradually shrank as the cycles were repeated, probably because of the precipitation of certain carbide or other compounds.
- 宇部工業高等専門学校の論文
- 1967-03-31
著者
関連論文
- 英国における材料摩耗研究の一調査
- 高クロム鋳鉄のころがり疲労強度特性
- ポットミルを用いた高クロム鋳鉄及び高炭素高速度鋼系合金の耐摩耗性評価と靭性
- ポットミルを用いた高クロム鋳鉄及び高炭素高速度鋼系合金の耐摩耗性評価と靭性
- 被削性を改良した鉛, 硫黄添加高クロム鋳鉄の硬さ, 耐摩耗性及び圧縮強度特性
- 高炭素高速度鋼系合金のころがり疲労
- 高炭素高速度鋼系合金の熱処理特性に及ぼす合金元素の影響
- 高炭素高速度鋼系合金のころがり疲労
- 高炭素高速度鋼系合金の熱処理特性に及ぼす合金元素の影響
- ポットミルを用いた金属材料の摩耗試験
- 高クロム鋳鉄のヤング率
- 高炭素高速度鋼系合金の耐摩耗性に及ぼす熱処理条件の影響
- 焼入れ焼戻し 高炭素高速度鋼系合金の耐摩耗性に及ぼす化学組成と試験条件の影響
- 高クロム鋳鉄の被削性に及ぼす鉛・硫黄添加の影響
- 高炭素高速度鋳鋼の熱処理及びころがり疲労特性
- 高炭素ハイス系合金の熱処理特性に及ぼす合金元素の影響
- ハイス系鋳造ロール材とSUS304との摩擦磨耗特性
- 鉛, 硫黄添加高クロム鋳鉄の機械的性質
- 鉛, 硫黄添加高クロム鋳鉄の被削性
- 高クロム鋳鉄の熱処理と被削性
- ハイス系合金のころがり疲労特性と耐食性
- 環境制御教育に関する研究(1) : 大気汚染
- フェライト質片状黒鉛鋳鉄の熱膨張式について
- 高クロム鋳鉄の熱処理特性に及ぼすMn,Ni,Cuの影響
- フェライト質黒鉛鋳鉄の成長について
- 鋼の乾燥摩耗におよぼす湿度の影響
- 球状黒鉛鋳鉄の成長について
- 鋳鉄の成長について