機能性のp-ビニル安息香酸グリシジル(GPVB)の合成とポリGPVB及びコーポリGPVB-MMAの物理的性質(第1報)
スポンサーリンク
概要
- 論文の詳細を見る
Physical properties of the two kinds of polymer, i.e., the polymer of GPVB in which the crosslinking agent Methylhexahydrophthalic acid anhydride (MHHPA) or Triethylenetetramine (TETA) is added to GPVB, and the polymer of GPVB-MMA (Methylmethacrylate) in which the crosslinking agent MHHPA or TETA is added to MMA-GPVB, are as follows : (1) The polymer with 0.76 mol of MHHPA per 1 mol of GPVB, showed the highest physical value on the following terms : a : Transverse strength; 1,300kg/cm^2 b : Elastic regain; 25,000kg/cm^2 c : Compressive strength; 3,100kg/cm^2 d : Rockwell hardness; 80 (30W) (2) The polymer with 1.0/6mol of TETA per 1 mol of GPVB, showed the highest physical value on the following terms : a : Transverse strength; 1,600kg/cm^2 b : Elastic regain; 33,000kg/cm^2 c : Compressive strength; 3,000kg/cm^2 d : Rockwell hardness; 80 (30W) (3) The polymer with different ratio of GPVB and MMA, with 0.76mol of MHHPA per 1mol of GPVB, showed the highest value of Transverse strength 1,600kg/cm^2 when it contained 20mol percent of GPVB. Elastic regain of the polymer was constantly 25,000kg/cm^2 with no relation to the mol percent of GPVB. About the other physical properties, the polymer gave the higher value with the more mol percent of GPVB. (4) The polymer with different ratio of GPVB and MMA, with 1.0/6mol of TETA per 1 mol of GPVB, showed the highest value of Transverse strength 1,700kg/cm^2 when it contained 20mol percent of GPVB. About the other physical properties, the polymer gave the higher value with the more mol percent of GPVB. (5) The polymer without crosslinking agent showed the lower value of the physical properties with the more GPVB. As Conclusion, when MHHPA or TETA are added, the polymer of GPVB and GPVB-MMA showed higher value of physical properties than that of PMMA (Poly-methylmethacrylate). These polymers have shown good value of physical properties and we expect it to be the hopeful materials of organic high molecule.
- 東海大学の論文
著者
関連論文
- P-36 ポリメタクリレートの構造と物性に関する研究(その9) : 3成分系モノマーの相図とポリマーのモルフォロジーについて
- A-22 P-ビニル安息香酸グリシジルによる合成シリカゲルの表面処理効果
- 6.ブタジエンジメタクリレートを架橋剤としたポリメタクリレートの物性(日本歯科理工学会 近畿・中四国, 九州2支部共催学術講演会)
- 付加型シリコーンゴムと樹脂との接着に関する研究
- 付加型シリコーン用プライマーの合成
- α-シアノメチルメタクリレートのラジカル重合における立体規則性生長の溶媒効果
- 芳香族系メタクリル酸エステルの立体規則性 : ラジカル重合における立体規則性生長の溶媒と温度効果
- 機能性のp-ビニル安息香酸グリシジル(GPVB)の合成とポリGPVB及びコーポリGPVB-MMAの物理的性質(第1報)
- フェニルメタクリレートのラジカル重合における立体規則性生長の溶媒効果
- トリチルメタクリレートのラジカル重合における立体規則性生長の溶媒効果
- β-cyanoethylmethacrylateのラジカル重合における立体規則性生長の溶媒効果(第1報)
- シリカ系無機質を芯として作ったメタクリレートマイクロカプセルの機械的強度について
- メチルメタクリレートにアルキレンジメタクリレートで高密度に架橋して作製したポリマーの機械的強度について