2 1/4Cr-1Mo鋼溶接部の800Kにおける低延性破壊

スポンサーリンク

概要

• 論文の詳細を見る

• The grain boundary fracture was investigated for the simulated weld HAZ with the various size of austenite grain. Two methods of cracking tests were employed ; the constant load and the constant extensional rate of the specimen. The former was the ordinary creep rupture test, and the later has been newly proposed in order to simulate the phenomena of fracture along the prior-austenite grain boundary. The grain size affects the crack-initiating time and the fracture mode. The grain boundary fracture was observed at two different extensional rates, that is, about 20 and 0.02 nm/s. The cracking test with the constant extensional rate was useful to examine the grain boundary embrittling during reheating.

• 三重大学の論文

著者

• 鈴木 英幸

  Department Of Mechanical Engineering Faculty Of Engineering Mie University

• 玉置 維昭

  Department of Mechanical Engineering, Faculty of Engineering, Mie University

• 鈴木 実平

  Department of Mechanical Engineering, Faculty of Engineering, Mie University

関連論文

• 1Cr-1/2Mo鋼溶接部における応力によるりんの偏析および粒界割れ
• Cr-Mo鋼HAZの焼もどし脆化におよぼす冶金学的因子の影響
• Cr-Mo鋼HAZの低延性クリープ破壊の防止における応力除去焼なましの効果
• 2 1/4Cr-1Mo鋼のHAZに観察されるSR脆化および焼きもどし脆化
• 鋼溶接部のクリープ脆化再現装置
• 電磁圧接装置とそのアルミニウムへの応用
• アルミニウムの冷間圧接
• セラミック切削工具の損傷特性に関する研究
• 2 1/4Cr-1Mo鋼溶接部の800Kにおける低延性破壊
• 鋼の過熱過程におけるオーステナイト結晶粒の形成および粒界偏析
• 2 1/4Cr-1Mo鋼溶接部の脆化および延性低下におよぼす顕微鏡組織の影響
• Cr-Mo鋼溶接部の焼きもどし脆化因子について
• 紡績機用の針の機械的性質におよぼす熱処理条件の影響
• Fe-P-C合金における急速α/γ変態に起因するりんの粒界偏析

もっと見る 閉じる

スポンサーリンク