Modification of AISI 304 Stainless Steel Surface by the Low Temperature Complex Salt Bath Nitriding at 430℃

スポンサーリンク

概要

• 論文の詳細を見る

• Salt bath nitriding of type 304 austenite stainless steels conducted at low temperature, 430°C, using a complex salt bath heat-treatment. Microstructure and the properties of the nitrided surface were systematically evaluated. Experimental results revealed that when 304 stainless steel subjected to complex salt bathing nitrided at such temperature less than 4 hours, the main phase of the nitrided modify layer was the expanded austenite (S phase) generally. When the treatment times prolonged up to 8 hours and more, S phase was formed and subsequently transformed partially into CrN, and then the secondary CrN phase precipitated. All treatments can effectively increase the surface hardness. And the nitrided layer depth thickened intensively with the increasing nitriding time. The growth of the nitrided layers took place mainly by nitrogen diffusion according to the expected parabolic rate law. Low temperature nitriding can improve the corrosion resistance against diluted hydrochloric acid. After nitriding for 16 hours, the sample has the best corrosion resistance than others though there are many CrN transformed in the layer.

• The Iron and Steel Institute of Japanの論文
• 2012-06-15

著者

• Wang Jun

  School Of Chemistry & Chemical Engineering Jinan University

• YAN Jing

  Southwest Oil and Gasfield Company Research Institute of Natural Gas

• LIN Yuanhua

  State Key Lab of Oil and Gas Reservoir Geology and Exploitation, Southwest Petroleum University

• WANG Jun

  School of Manufacturing Science and Engineering, Sichuan University

• ZENG Dezhi

  State Key Lab of Oil and Gas Reservoir Geology and Exploitation, Southwest Petroleum University

• HUANG Runbo

  School of Manufacturing Science and Engineering, Sichuan University

• HU Zejing

  School of Manufacturing Science and Engineering, Sichuan University

関連論文

• Characteristic Features of Rolling Texture Development in FCC Alloys Low Having Very Stacking Fault Energies
• Effects of Secondary Flow on the Electromagnetic Separation of Inclusions from Aluminum Melt in a Square Channel by a Solenoid
• The Effect of Long-Term Isothermal Aging on Dynamic Fracture Toughness of Type 17-4 PH SS at 350℃
• A Highly Sensitive and Rapid Assay for Protein Determination in Human Urine and Penicillin Using a Rayleigh Light-Scattering Technique with Benzeneazo-8-acetylamino-1-naphthol-3,6-disulfonic Acid Sodium Salt
• A Novel Method to Remove Iron Impurity from Aluminum
• Removal of Non-Metallic Inclusions from Aluminum by Electroslag Refining
• A compact quad-band bandstop filter using dual-plane defected structures and open-loop resonators
• Tailoring the Size Distribution of Ag Nanoparticles Embedded in SiO_2 by Xe Ion Postirradiation
• Modification of AISI 304 Stainless Steel Surface by the Low Temperature Complex Salt Bath Nitriding at 430℃

スポンサーリンク