Microwave Carbo-thermal Reduction for Recycling of Cr from Cr-containing Steel Making Wastes
スポンサーリンク
概要
- 論文の詳細を見る
In this study, Cr-containing steel making slag and pickling sludge were reduced with graphite by microwave (MW) heating. The reduced metal (alloy) particles were obtained and their compositions were determined. Pure Cr2O3 was reduced at lower temperature than expected from thermodynamics.Fundamental studies on MW heating of Cr2O3 were performed using a multi-mode and a single mode MW applicators in order to investigate the enhanced reaction kinetics. It was demonstrated that heating of Cr2O3 requires incubation period before onset of the sudden temperature rise. Cr2O3 was preferentially heated in the electric (E-) field of MW and metal pieces were formed.It was pointed out that the MW heated specimen had inhomogeneous temperature distribution, the temperature could be measured at the localized region and/or it is an average of the temperature distribution in a miro-scale. The reduction might have occurred in the high temperature region, preferentially. In order to account for generation of the inhomogeneous distributions, two possibilities are considered. First, as the enhanced heating behavior in E-field, dielectric heating mechanism of Cr2O3 is likely, and its permittivity (loss factor) has large temperature dependence. Therefore, small initial temperature fluctuation was amplified to become the local temperature difference (hot spot). Second, occurrence of local arcing enhanced the kinetics and formation of metal pieces.
- 社団法人 日本鉄鋼協会の論文
- 2008-05-15
著者
-
Taniguchi Shoji
Tohoku Univ. Sendai Jpn
-
Taniguchi Shoji
Graduate School Of Engineering Tohoku University
-
Taniguchi Shoji
Graduate School Of Environmental Studies Tohoku University
-
Sasaki You
Tohoku University
-
Yoshikawa Noboru
Graduate School Of Environmental Studies Tohoku University
-
MASHIKO Ken-ichi
Tohoku University
-
TODOROKI Hidekazu
Yakin Kawasaki Co. Ltd. Technical Research Center
-
Todoroki Hidekazu
Technical Res. Centre Nippon Yakin Kogyo Co. Ltd.
関連論文
- Microwave Sintering of Ni-Based Bulk Metallic Glass Matrix Composite in a Single-Mode Applicator
- Microstructural Changes during Microwave Heating of Ni_Zr_Nb_Ti_Pt_ Metal Glasses
- Kinetics Evaluation of Inclusions Removal during Levitation Melting of Steel in Cold Crucible
- Utilization of Al Scrap for Fabrication of Al(alloy)/Al_2O_3 Composite Material
- Electromagnetic Flow around Two Non-conducting Particles and the Interaction Forces : Different Diameter Cases
- Crack Generation in Blast Furnace Slag Bearing High Titanium by Microwave Cyclic Heating
- Brief Review on Microwave (MW) Heating, Its Application to Iron & Steel Industry and to the Relevant Environmental Techniques
- Application of Microwave Heating Techniques to Steel Industry and to Environmental Problems
- Microwave Magnetic Field Heating of a Cobalt-Based Amorphous Ribbon
- Preface to the Special Issue on "Advanced Application of Electromagnetic Force to Materials Processing"
- Application of Microwave Technique for Dehydration of Sludge Generated in a Stainless Steel Plant
- Microwave Carbo-thermal Reduction for Recycling of Cr from Cr-containing Steel Making Wastes
- Fabrication of Composite Materials Using Al Scrap and Wasted Glass
- Heating of Metal Particles in a Single-Mode Microwave Applicator
- Growth Rate of Reaction Layer between SiO_2 and Molten Al above 1473K
- Application of Microwave Heating to Reaction between Soda-Lime Glass and Liquid Al for Fabrication of Composite Materials
- Prospects for the Control of Solidification Structures from the Viewpoints of Weld, Hot-workability and Near Net Shape Casting
- Model Experiment on Inclusion Removal by Bubble Flotation Accompanied by Particle Coagulation in Turbulent Flow
- Application of Extreme Value Analysis for Two- and Three-Dimensional Determinations of the Largest Inclusion in Metal Samples
- Electromagnetic Separation of Nonmetallic Inclusion from Liquid Metal by Imposition of High Frequency Magnetic Field
- Particle-Size-Grouping Method of Inclusion Agglomeration and its Application to Water Model Experiments
- Application of Statistics of Extreme Vaules for Inclusions in Stainless Steel on Different Stages of Steel Making Process
- Dehydration Behavior of Goethite Blended with Graphite by Microwave Heating
- Particle Coagulation in Molten Metal Based on Three-Dimensional Analysis of Cluster by X-Ray Micro-Computer Tomography (CT)
- Morphology of Nonmetallic-inclusion Clusters Observed in Molten Metal by X-ray Micro-Computed Tomography (CT)
- Microwave Heating Behavior of Blast Furnace Slag Bearing High Titanium