Change of phase compositions in calcia stabilized zirconia ceramics using a boric acid additive
スポンサーリンク
概要
- 論文の詳細を見る
Dense calcia-stabilized zirconia (CSZ) ceramics were prepared by using a small amount of boric acid (H3BO3) as the sintering additive at the sintering temperature of 1700°C. The effect of H3BO3 content on the sintering behavior, the change of phase composition and mechanical properties of the CSZ ceramics were mainly investigated. The results showed that, due to the reaction between B2O3 and CaO, borate liquid was formed during the sintering, which promoted the the densification of CSZ ceramics. Meanwhile, the depletion of the CaO from the lattice of CSZ ceramics resulted in the phase transformation of ZrO2. The content of tetragonal ZrO2 phase increased with increasing the H3BO3 content. So the phase composition of CSZ ceramics could be well controlled by adjusting the amount of H3BO3. The bending strength and fracture toughness of the sintered CSZ ceramics also increased with increasing the H3BO3 content, namely the content of tetragonal ZrO2 phase, which had better mechanical properties, and the highest value reached 267 MPa and 3.35 MPa·m1/2, respectively.
- 公益社団法人 日本セラミックス協会の論文
- 2009-04-01
著者
-
Chen Fei
State Key Laboratory Of Advanced Technology For Materials Synthesis And Processing Wuhan University
-
Zhang Lianmeng
State Key Laboratory Of Advanced Technology For Materials Synthesis And Processing Wuhan University
-
Zhang Lianmeng
State Key Lab Of Advanced Technology For Materials Synthesis And Processing Wuhan University Of Tech
-
SHEN Qiang
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University
-
CHEN Changlian
State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Tec
-
LI Junguo
State Key Lab of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Tec
-
Li Junguo
State Key Lab Of Advanced Technology For Materials Synthesis And Processing Wuhan University Of Tech
-
Shen Qiang
State Key Laboratory Of Advanced Technology For Materials Synthesis And Processing Wuhan University
-
Chen Changlian
State Key Lab Of Advanced Technology For Materials Synthesis And Processing Wuhan University Of Tech
-
Chen Fei
State Key Lab of ASIC and Systems, Department of Microelectronics, Fudan University, Shanghai 200433, China
関連論文
- Preparation and Thermoelectric Properties of Bi-Doped Mg_2Si_Sn_ Compound
- Change of phase compositions in calcia stabilized zirconia ceramics using a boric acid additive
- Preparation of pore gradient silicon nitride ceramics by a high-velocity oxy-fuel spraying technique
- Effect of Self-Dispersion Nanosized AlOOH on Microstructure and Wear Resistance of Alumina Ceramic Balls
- Composite Dispersion of Nanosized AlOOH in Liquid Phase
- Density Functional Theory Study of Cu Adhesion on Rh, Ir, Pd, Ta, Mo, Ru, Co, and Os Surfaces
- Epitaxial Integration of (100) Bi4Ti3O12 with (0001) ZnO through Long-Range Lattice Matching
- Epitaxial Integration of (100) Bi_4Ti_3O_ with (0001) ZnO through Long-Range Lattice Matching