Bending Deformation of C_<60> Nanowhiskers in Solution and Air
スポンサーリンク
概要
- 論文の詳細を見る
The mechanical properties of C60 nanowhiskers (C60NWs) grown in a solution by a liquid-liquid interfatical precipitation method were investigated by a bending method. C60NWs in the solution exhibited large elastic deformation where they recovered for large bending with a curvature of 290 μm. On the other hand, C60NWs in air were broken even for small bending with only a 650 μm curvature. From the analysis of the bending, the yield stress or breaking stress for C60NWs in air is estimated to be 7.7 MPa, that is larger by one order compared with 0.7 MPa for bulk C60 crystals. In addition, it is shown that the Youngs modulus for C60NWs in the solution is 8.9 GPa, that is below a half of 20 GPa for bulk C60 crystals.
- 社団法人 電気学会の論文
- 2008-08-01
著者
-
TACHIBANA Masaru
International Graduate School of Arts and Sciences, Yokohama City University
-
Tachibana Masaru
International Graduate School Of Arts And Sciences Yokohama City University
-
Kojima Kenichi
International Graduate School Of Arts And Sciences Yokohama City University
-
WATANABE Mami
International Graduate School of Arts and Sciences, Yokohama City University
-
Watanabe Mami
International Graduate School Of Arts And Sciences Yokohama City University
関連論文
- Structural Analysis of C_ Nanotubes Heat-Treated in Vacuum
- Bending Deformation of C_ Nanowhiskers in Solution and Air
- Evidence for the Presence of Fullerene in Diesel Soot Using Laser Desorption/Ionization Mass Spectrometry
- Anomalous Anderson Weak Localization of Graphite Thin Film Fabricated by Plasma-Enhanced Chemical Vapor Deposition