Effect of High-temperature Field on Supersonic Oxygen Jet Behavior
スポンサーリンク
概要
- 論文の詳細を見る
In the steelmaking process, the behavior of the top blown oxygen jet is an important factor for controlling BOF or EAF operation. Because the temperature in the BOF is very high, jet behavior is still not fully understood. In this study, supersonic oxygen jet behavior in a high-temperature field was investigated by measuring the velocity and temperature of the oxygen jet in a heated furnace, and the results were compared with a jet model proposed by previous researchers. The results showed that velocity attenuation of the jet was restrained and the potential core length was extended in a high-temperature field. Under these experimental conditions, the results were in good agreement with the jet model using Pr=0.715 and Sc=0.708 proposed by Kleinstein. Supersonic jet behavior for SCOPE-JET nozzle, which can be applied in EAF operation to obtain high-energy efficiency, was also investigated. SCOPE-JET had a long potential core and attenuation of the jet in the axial direction was extremely restrained. It was shown to be possible to obtain the jet behavior of SCOPE-JET nozzle using the jet model with the adiabatic flame temperature as the ambient temperature and appropriate temperature attenuation behavior in the axial direction.
- 社団法人 日本鉄鋼協会の論文
- 2006-09-15
著者
-
SUMI Ikuhiro
Technology Planning Department, Head office, JFE Steel Corp.
-
Sumi Ikuhiro
Technology Planning Department Head Office Jfe Steel Corp.
-
Kishimoto Yasuo
Steelmaking Research Department Steel Research Laboratory Jfe Steel Corp.
-
Kishimoto Yasuo
Steelmaking Research Dept. Steel Research Laboratory Jfe Steel Corporation
-
SUMI Ikuhiro
Steelmaking Research Dept., Steel Research Laboratory, JFE Steel Corporation
-
Igarashi Hiroshi
Yamanashi Laboratories Development & Engineering Taiyo Nippon Sanso Corporation
-
Kikuchi Yoshiteru
Steelmaking Research Dept. Steel Research Laboratory Jfe Steel Corporation
関連論文
- Micro-structure Refinement in Low Carbon High Manganese Steels through Ti-deoxidation : Austenite Grain Growth and Decomposition
- Micro-structure Refinement in Low Carbon High Manganese Steels through Ti-deoxidation-Inclusion Precipitation and Solidification Structure
- Interface Migration Behavior of the δ→γ Interface in Low Carbon High Manganese Steel Samples De-oxidized with Ti or Al
- Effect of Ti De-oxidation on Solidification and Post-solidification Microstructure in Low Carbon High Manganese Steel
- Prediction of Equiaxed Crystal Ratio in Continuously Cast Steel Slab by Simplified Columnar-to-Equiaxed Transition Model
- Effect of Flux Dispersion Behavior on Desulfurization of Hot Metal
- Behavior of Top-Blown Jet under Reduced Pressure
- Effect of High-temperature Field on Supersonic Oxygen Jet Behavior
- Micro-structure Refinement in Low Carbon High Manganese Steels through Ti-Deoxidation, Characterization and Effect of Secondary Deoxidation Particles