Laser-ultrasonic Monitoring of Austenite Recrystallization in C-Mn Steel

スポンサーリンク

概要

• 論文の詳細を見る

• The static recrystallization kinetics of hot deformed austenite were characterised by a combination of in-situ laser-ultrasonics and stress relaxation measurements. Samples were deformed in compression at temperatures of 850°C and 900°C. The applied strain was varied between 0.2 and 0.5, whilst the strain rates used were 0.1 s−1 and 0.5 s−1. At various points during annealing samples were quenched and analysed by optical microscopy.During recovery prior to recrystallization the ultrasonic velocity change and attenuation were almost constant. During recrystallization, the velocity change and attenuation decreased for the conditions imposed. The decrease in velocity change was mostly due to a change in the overall texture. The decrease in attenuation could be explained by a change in grain size. Unfortunately, the additional effect of dislocation damping on attenuation could not be quantified.Comparison of the stress relaxation kinetics with the observed decrease in ultrasonic velocity change and attenuation generally showed good agreement.From the attenuation measurements the grain sizes in the recrystallised structure for various applied strains were calculated. Comparison with grain sizes determined from optical microscopy showed reasonable agreement considering the accuracy of the attenuation measurements and the assumptions made.

• 社団法人 日本鉄鋼協会の論文
• 2006-08-15

著者

• van der

  Faculty of Applied Science, Kavli Institute of Nanoscience Delft, Delft University of Technology

• SMITH Ali

  Netherlands Institute for Metals Research

• Van Der

  Faculty Of Aerospace Engineering Delft University Of Technology

• Sietsma Jilt

  Imi-national Research Council Of Canada

• KRUGER Silvio

  Department of Materials Science & Engineering, Delft University of Technology

• Kruger Silvio

  Department Of Materials Science & Engineering Delft University Of Technology

関連論文

• 量子ドットの近藤効果(近藤効果はめぐる : 近藤効果40周年)
• Recovery Processes in the Ferrite Phase in C-Mn Steel
• Port-controlled Hamiltonian Systems:Towards a Theory for Control and Design of Nonlinear Physical Systems (ミニ特集 ロバスト非線形制御)
• Effect of Inhomogeneous Deformation on the Recrystallization Kinetics of Deformed Metals
• Laser-ultrasonic Monitoring of Austenite Recrystallization in C-Mn Steel
• Stacking of Single-Grain Thin-Film Transistors
• NUMERICAL SIMULATION OF LONG-PERIOD WAVES AND SHIP MOTIONS IN TOMAKOMAI PORT, JAPAN

スポンサーリンク