金属粉末射出成形法によるロバスト性の高いSKD11の創製
スポンサーリンク
概要
- 論文の詳細を見る
We studied the mix proportion percentage of the gas atomized powder and the water atomized powder in order to develop the wide sintering temperature for SKD11 materials. As a result, the mass production of the high precision SKD11 sintered compacts which were affected by the temperature difference in the sintering furnace became possible. The precision of the sintered compacts with mixed powders was ±0.22% (L=19 mm). Also, tensile strength was 1600∼1800 Mpa transeverse rupture strength was 3400∼3600 MPa, impact value was 23∼32 KJ/m2 and fatigue strength was 456 MPa.
- 2005-10-15
論文 | ランダム
- Magnetic Properties of Intermetallic Compound Mn_Ge_8
- Role of Skeletal Muscle Metabolism in Exercise Capacity of Patients With Myocardial Infarction Studied by Phosphorus-31 Nuclear Magnetic Resonance
- PREDICTING OUTCOME OF NON・SUPERVISED HOME EXERCISE TRAINING IN PATIENTS AFTER ACUTE MYOCARDIAL INFARCTION (AMI) : PHYSICAL STATUS IS ONE OF THE STRONGEST PREDICTORS
- Synthesis of Pseudodeflectusin and Ustusorane C : Structural Revision of Aspergione A and B
- Novel classification based on immunohistochemistry combined with hierarchical clustering analysis in non-functioning neuroendocrine tumor patients