Electron-Beam Domain Writing in Stoichiometric LiTaO3 Single Crystal by Utilizing Resist Layer
スポンサーリンク
概要
- 論文の詳細を見る
Ferroelectric crystals with patterned domain structures, such as LiTaO3, show excellent optical properties and have thus been used as materials for functional photonic devices. The effect of a resist layer on microscale domain engineering by electron-beam direct writing was examined using stoichiometric LiTaO3 single crystals. It was demonstrated that using an electron-beam (e-beam) resist to spatially confine the beam electrons, a regular, uniform dot array of domains (with a size of 1 μm) could be fabricated along the $z$-axis throughout the crystal. Ring-shaped domains could be fabricated by this technique. Our experiments pave the way for improving the e-beam domain fabrication method by utilizing a resist covering.
- Japan Society of Applied Physicsの論文
- 2006-04-25
著者
-
KITAMURA Kenji
National Institute for Materials Science
-
Terabe Kazuya
National Institute For Materials Science
-
Hatano Hideki
National Institute For Materials Science
-
Li Xijun
National Institute For Materials Science
-
Kitamura Kenji
Advanced Materials Laboratory National Institute For Materials Science (nims)
-
Kitamura Kenji
National Institute For Research In Inorganic Materials
関連論文
- A Ta_2O_5 Solid-electrolyte Switch with Improved Reliability(Session3: Emerging Devices I)
- A Ta_2O_5 Solid-electrolyte Switch with Improved Reliability(Session3: Emerging Devices I)
- Blue photoluminescence of germania-stabilized benitoite(Glass and Ceramic Materials for Photonics)
- Afterglow in synthetic bazirite, BaZrSi_3O_9
- Preparation of a Clay Pillared with Rodlike Cationic Polysiloxane
- A Novel Synthetic Route to Layered Double Hydroxides Using Hexamethylenetetramine
- Growth and Properties of A15-type Nb_3Sn Single Crystals
- Solid-Electrolyte Nanometer Switch(Novel Device Architectures and System Integration Technologies)
- Preparation of Nitrogen-doped Anatase Titania by Treatment of Layered Titania/Isostearate Nanocomposite with Aqueous Ammonia
- Volume Holographic Storage in Near-Stoichiometric LiNbO_3:Ce, Mn