低炭素鋼の時効中の炭化物形成におよぼす添加元素の影響についてのモデル化からの検討(物理的性質)
スポンサーリンク
概要
- 論文の詳細を見る
Over aged samples with Mo added steel after quenching show high tensile strength than that of without Mo steel and show peculiar BH curve plotted against over aging time. To analyze these phenomena, kinetic model for carbide precipitation was derived, which deal with both cementite and cluster. The following results are obtained. (1) Low carbon steel with Mo, clusters are formed at room temperature after quenching. The site number used for cluster is 10^<15>/mm^3, which indicates Mo-C dipole is considerd to be the site of cluster nucleation. Clusters are dissolved with the aging temperature at 200℃ in short time. (2) Clusters are dissolved during BH treatment (170℃×20min), which reduce the BH value for the sample without over aging. On the othe hand, the drop of BH with 200℃×10min over aging is lower, because clusters are dissolved during over aging. This causes that BH plotted against aging time shows the curve with peak. (3) The strength by calculation in the case of lower carbon show less value than that of higher carbon case, because cluster nucleation rate deeply depends on carbon content.
- 社団法人日本鉄鋼協会の論文
- 2006-06-01
著者
関連論文
- 284 タンディッシュ上ノズル Ar 流量自動制御技術(凝固基礎・連鋳介在物 (II), 製鋼, 日本鉄鋼協会第 112 回(秋季)講演大会)
- スウェーデン留学体験記
- テーラードブランク材のエリクセン値に及ぼす熱影響部軟化の影響
- 低炭素鋼の時効中の炭化物形成におよぼす添加元素の影響についてのモデル化からの検討(物理的性質)
- 極低炭素鋼板の歪時効速度に及ぼすMnの影響(力学特性)
- 高強度鋼板の剪断加工性
- 低炭素鋼の過時効後の時効特性に及ぼすMoの影響(物理的性質)
- 極低炭素BH鋼板の歪時効速度に及ぼすMoの影響
- 界面エネルギーを考慮したγ相中での Nb 炭窒化物の析出挙動の定式化
- γ域, α域における炭窒化物の析出挙動の定式化