Hardness Based Creep Life Prediction for 2.25Cr-1Mo Superheater Tubes in a Boiler
スポンサーリンク
概要
- 論文の詳細を見る
In the present work, the applicability and limitation of a hardness based approach to evaluate creep strength of boiler tubes fabricated from 2.25Cr–1Mo steel have been examined. For superheater tubes in a boiler, a screening technique to judge the damage level would be useful since the number of tubes to be assessed is numerous. It was confirmed that creep strength of tube materials was well correlated with hardness independently of service histories. However, the obtained relationship should not be extended to hardened materials associated with higher dislocation densities. It was found that cold work prior to creep tests remarkably decreased rupture lives despite high hardness values. The extent of change in precipitates, in terms of carbides spherodization and growth of PFZ, was more pronounced in a pre-strained material, presumably due to contribution of pipe diffusion. A similar tendency is also observable in quenched and tempered 2.25Cr–1Mo plate materials, in which densely populated dislocations were introduced at fabrication. For the critical judgement, a more straightforward method, for example examining the removed tubes in service in an iso-stress manner, should be employed. However, time consuming and expensive tests do not necessarily generate reliable answers. Since a test piece machined from an actual boiler tube inevitably has got a small cross-sectional area, rupture life in air is significantly reduced by oxidation. The metal loss, which is a function of temperature and testing duration, can be larger in a test at low temperature rather than that in a short-term test at high temperature. Metal loss at failure for an iso-stress tested specimen can be reduced with increase in testing temperature, suggesting that a creep test under accelerating temperature can derive more realistic prediction.To evaluate the genuine creep strength, the rupture lives in NIMS database obtained in air were converted into those in vacuum using the damage mechanics by Kachnov and Rabotnov. The following equation was obtained to predict the rupture life in vacuum on the basis of hardness measurement prior to service.<center>Larson Miller Parameter (LMP) =(log trv+20)T=18 858−6 183 log(σ/Hvo)−1 807 log2(σ/Hvo)</center>where trv is the rupture life in vacuum, T is the temperature in Kelvin and Hvo is the Vickers hardness.
- 2006-02-15
著者
-
Fujibayashi Shimpei
Engineering Designe & Technical Department Idemitsu Engineering Co. Ltd.
-
Fujibayashi Shimpei
Engineering Center Idemitsu Engineering Co. Ltd.
-
ISHIKAWA Yuuji
Inspection & Reliability Section, Chiba Refinery, Idemitsu Kosan Comapny
-
ARAKAWA Yoshiaki
Inspection & Reliability Section, Chiba Refinery, Idemitsu Kosan Comapny
-
Ishikawa Yuuji
Inspection & Reliability Section Chiba Refinery Idemitsu Kosan Comapny
-
Arakawa Yoshiaki
Inspection & Reliability Section Chiba Refinery Idemitsu Kosan Comapny
-
FUJIBAYASHI Shimpei
Engineering Center
関連論文
- Life Prediction of Low Alloy Ferritic Steels Based upon the Tertiary Creep Behavior
- Hardness Based Creep Life Prediction for 2.25Cr-1Mo Superheater Tubes in a Boiler
- A Comparative Study on the Θ Projection and the Ω Method
- Cross-weld Creep Behavior and Life Prediction of Low Alloy Ferritic Steels
- Creep Behavior of 2.25Cr-1Mo Steel Shield Metal Arc Weldment
- Effect of Carbide Morphology on the Susceptibility to Type IV Cracking of a 1.25Cr-0.5Mo Steel
- Creep Behavior at the Intercritical HAZ of a 1.25Cr-0.5Mo Steel
- The Effect of Grain Boundary Cavities on the Tertiary Creep Behavior and Rupture Life of 1.25Cr-0.5Mo Steel Welds
- Grain Boundary Damage Evolution and Rupture Life of Service-exposed 1.25Cr-0.5Mo Steel Welds
- Creep Behavior and Rupture Life of the Simulated Intercritical HAZ for 1.25Cr-0.5Mo Steel under a Multiaxial Stress State