TG/DTA-MS測定条件の最適化と材料分析への応用

概要

論文の詳細を見る
Direct coupling of TG/DTA to MS is achieved using a capillary tube as interface. Inner diameter and length of the capillary tube are optimized to 0.25 mm and 5 m, respectively. The period necessary to start the measurement after setting a new sample into the TG/DTA is minimized to 10 minutes by increasing the initial purge gas flow rate to 1000 ml min-1. Quantitative MS analysis of calcium oxalate is achieved. The repeatability of measurements are ±1.5% for CO2 and ±6.1% for H2O. Analysis in He + 20% O2 atmosphere is proved to be fully possible and effective to understand the thermal behavior of the samples in air.Examples of TG/DTA-MS results for various materials are reported; polymers (nylon-6, high-density polyethylene and polystyrene), a clay, mineral (sepiolite), and PYREX glass are measured and their thermal behavior are understood clearly and quickly.