A Crack Growth Evaluation Method for Interacting Multiple Cracks

スポンサーリンク

概要

• 論文の詳細を見る

• When stress corrosion cracking or corrosion fatigue occurs, multiple cracks are frequently initiated in the same area. According to section XI of the ASME Boiler and Pressure Vessel Code, multiple cracks are considered as a single combined crack in crack growth analysis, if the specified conditions are satisfied. In crack growth processes, however, no prescription for the interference between multiple cracks is given in this code. The JSME Post-Construction Code, issued in May 2000, prescribes the conditions of crack coalescence in the crack growth process. This study aimed to extend this prescription to more general cases. A simulation model was applied, to simulate the crack growth process, taking into account the interference between two cracks. This model made it possible to analyze multiple crack growth behaviors for many cases (e. g. different relative position and length) that could not be studied by experiment only. Based on these analyses, a new crack growth analysis method was suggested for taking into account the interference between multiple cracks.

• 一般社団法人日本機械学会の論文
• 2003-01-15

著者

• Kamaya Masayuki

  Institute Of Nuclear Safety System Inc.

• Kamaya Masayuki

  Institute For Nuclear Safety System Inc.

関連論文

• Angular Distribution of Slip Steps by Three-Dimensional Polycrystalline Model for Stainless Steel
• Fatigue Damage Evaluation Using Electron Backscatter Diffraction
• A Smoothing Filter for Misorientation Mapping Obtained by EBSD
• A Crack Growth Evaluation Method for Interacting Multiple Cracks
• Plastic Strain Measurement by EBSD
• Stress Intensity Factors of Surface Crack with Undulated Front
• J-Integral Solutions for Surface Cracks Inside Pipes under Internal Pressure

スポンサーリンク