Mechanical Properties of Welded Joints of 780MPa Grade Ultra-fine Grained Steels
スポンサーリンク
概要
- 論文の詳細を見る
Three kinds of 780 MPa grade ultra-fine grained steels with different chemical composition were produced by warm rolling. The steels were characterized by ultra-fine ferrite grains (less than 1 μm). With the steels strength-overmatching welded joints were prepared, and their mechanical properties were investigated. It is found that softening occurred in the heat-affected zone (HAZ) because of the coarsening of ferrite grains due to welding heat input. However, by using low welding heat input and strength-overmatching weld metal, the detrimental effect of softening on strength was restrained, and welded joints with strength equivalent to that of base metal were obtained. The deformability of welded joints was found to be related to the yield ratio (yield strength / tensile strength) of base metal. Low yield ratio is desirable to the deformability of welded joints. The HAZs in the welded joints of low welding heat input of 10 kJ/cm have good impact toughness for all the steels. Except for 0.14C-0.30Si-1.46Mn steel, the HAZs in the welded joints formed from the other two steels also have good impact toughness for welding heat input of 20 kJ/cm, and their fracture appearance transition temperature (vTrs) of the HAZs is lower than −40°C, and their Charpy impact energy at −40°C exceeds 200 J.
- 社団法人 日本鉄鋼協会の論文
- 2003-12-15
著者
-
OHMORI Akio
Steel Reesearch Center, National Insitute for Materials Science
-
QIU Hai
Steel Research Center, National Institute for Materials Science
-
Qiu Hai
National Institute For Materials Science
-
Qiu Hai
Steel Research Center National Institute For Material Science
-
Ohmori Akio
Steel Research Center National Institute For Material Science
-
Hagiwara Yukito
Steel Research Center National Institute For Material Science
関連論文
- Serration of Grain Boundary in Ni-30Fe Alloy through High Temperature Deformation
- Precipitation of Carbonitrides and Their Strengthening upon Non-quench Aging for Micro-alloyed Acicular Ferrite Pipeline Steels
- Difference in the Role of Non-quench Aging on Mechanical Properties between Acicular Ferrite and Ferrite-Pearlite Pipeline Steels
- Evaluation of dynamic fracture toughness of welding heat-affected zone of structural steel
- Effect of Strain Rate and Plastic Pre-strain on the Ductility of Structural Steels
- Evaluation of Ductile Fracture of Structural Steels by Microvoid Model
- Development of a Three-dimensional Model for Ductile Fracture in Materials Containing Two Types of Microvoids
- The effect of environment temperature on the transformation of retained austenite in a weld metal
- Mechanical Properties of Welded Joints of 780MPa Grade Ultra-fine Grained Steels