Kinetics of the Reactions in Carbon Composite Iron Ore Pellets under Various Pressures from Vacuum to 0.1MPa
スポンサーリンク
概要
- 論文の詳細を見る
In order to clarify the mechanism of the complicated reactions in carbon composite iron ore pellets, carbon composite iron ore pellets of 3.5 mm in diameter were heated in the five conditions; (a) in vacuum, (b) the closed system after evacuation, (c)-(e) the closed system of initially 0.001, 0.01 and 0.1 MPa nitrogen after evacuation. The weight loss was measured in the five conditions (a)-(e) by gravimetric method. The individual curves were composed of the fast first step and the relatively slow second step. The first step was analyzed as zero order reaction and the rate constant, ks1, was obtained. The second step was analyzed by applying the rate equations for the diffusion control in the product shell of the shrinking core model for spherical iron ore particles. The applicability of the equations was pretty good. The rate con-stant, ks2, was a function of the total pressure pt and temperature T, which was expressed as ks2=A(pt)exp[−B(pt)/T]. The apparent activation energy was ranged from 195 to 280 kJ/mol, which is near the activation energy for the diffusivity of carbon in γ-iron. The rate of the fractional weight loss seems to be in a mixed control regime of the direct reduction, indirect reduction and indirect gasification. The transition fractional weight loss from the first step to the second step was evaluated in the conditions (a) and (b). It decreased with increasing the total pressure until it reached nearly zero in the conditions (c), (d) and (e), where Eq. (11) was applicable in the whole range of Ft.
- 社団法人 日本鉄鋼協会の論文
- 2004-12-15
著者
-
IGUCHI Yoshiaki
Nagoya Institute of Technology
-
Iguchi Yoshiaki
Nagoya Institute Of Technology Graduate School Department Of Materials Science And Engineering
-
YOKOMOTO Shohei
Nagoya Institute of Technology
関連論文
- Influence of sulfur activity on the reforming reaction during production of iron carbide with CO-CH_4-H_2-H_2S mixtures in fluidized bed
- Electronic Transport Properties of ZrTiO_4 at High Temperature ( FERROELECTRIC MATERIALS AND THEIR APPLICATIONS)
- Carburized Carbon Content of Reduced Iron and Direct Carburization in Carbon Composite Iron Ore Pellets Heated at Elevated Temperature
- Abnormal Swelling during Reduction of Binder Bonded Iron Ore Pellets with CO-CO_2 Gas Mixtures
- Reduction and Melting Process of Coal Char/Iron Ore Composite Pellet by Heating in Nitrogen
- Chromites Reduction Reaction Mechanisms in Carbon-Chromites Composite Agglomerates at 1773K
- Kinetics of Decomposition and Re-oxidation Resistance of θ- and χ-Iron Carbides at Elevated Temperatures and Influence of Their Formation Conditions
- Carburization Kinetics of Reduced Iron during Its Carbidization in CO-H_2-H_2O-H_2S Mixtures
- Reactions, Coalescence of Reduced Iron Particles, and Liberation of Carbon Particles in Carbon Composite Iron Ore Pellets
- Kinetics of the Reactions in Carbon Composite Iron Ore Pellets under Various Pressures from Vacuum to 0.1MPa
- Sulfur Sorption Rate and Equilibrium Content of Reduced Iron in H_2-H_2S Mixtures