Investigations of Sm_2Fe_<17> under High Pressures of Gaseous Phases.

スポンサーリンク

概要

• 論文の詳細を見る

• Samples of the Sm<SUB>2</SUB>Fe<SUB>17</SUB> alloy were exposed to hydrogen or nitrogen gas compressed to pressures between 1. 0 and 1. 5 GPa. Sample hydrogenated at 100<SUP>0</SUP>C and 1. 12 GPa (H<SUB>2</SUB>) pulverized completely but the crystalline structure did not differ from that obtained during hydrogenation at 1 MPa where pulverization does not occur. Nitriding reaction carried out at 350<SUP>0</SUP>C and 1. 0 GPa resulted in transition into nitride Sm<SUB>2</SUB>Fe<SUB>17</SUB>N<SUB>3</SUB>. The disproportionation of sample has occurred under high nitrogen pressure when heated at 600<SUP>0</SUP>C.

• 日本高圧力学会の論文
• 1998-00-00

著者

• Filipek S

  Institute Of Physical Chemistry Of The Polish Academy Of Sci.

• UCHIDA H.

  Department of Electrical & Electronic Engineering, Toyohashi University of Technology

• Ishiyama O.

  Materials And Structures Laboratory Tokyo Institute Of Technology

• Filipek S.M.

  Institute of Physical Chemistry of the Polish Academy of Sci.

関連論文

• Nonlinear spectroscopy of magnetization-induced second-harmonic generation in magneto-photonic crystals and microcavities
• Magnetic Garnet Thick Films Deposited with Aerosol Deposition Method for Optical Isolator(Selected papers from MORIS 2006 Workshop on Thermal & Optical Magnetic Materials and Devices)
• In situ Germination of Seeds under High Pressure Conditions
• Evidence for Preferential Digestion of Male-derived Chloroplast DNA in Young Zygotes of Chlamydomonas reinhardtii by Histochemical Immunogold Electron Microscopy
• A dizygotic, concordant isolated cleft palate twin pair : A case report : Papers Presented from Platform
• Investigations of Sm_2Fe_ under High Pressures of Gaseous Phases.

スポンサーリンク