オキシアルキルアミンを共存させた水酸化第1鉄の湿式酸化法による板状ゲータイト粒子の合成
スポンサーリンク
概要
- 論文の詳細を見る
The plate-like goethite particles were synthesized from a ferrous hydroxide solution with oxyalkylamine (OAA) in the course of oxidation. The ratio of the crystallite sizes of (010) and (110) direction, D<SUB>010</SUB>/D<SUB>110</SUB>, were determined and its correlation with particle morphology was discussed. The value of D<SUB>010</SUB>.D<SUB>110</SUB> was 1.3 times higher than the value calculated from a<SUB>0</SUB> and b<SUB>0</SUB> using Gibbs equation. It shows growth of the (100) plane was restricted due to adsorption of OAA. Titration of ferrous sulfate with NaOH in the presence of acicular or plate-like goethite particles show that formation of plate-like goethite particles is attributed to the prevention of crystal growth along c-axis. Synthesis of plate-like goethite is related to the preferred adsorption site of alcoholic part of OAA, since plate-like goethite particles have never been synthesized from ammonium. Adsorption of OAA on (100) and (001) decreases the rate of crystal growth of (100) and (001), especially when free OAA concentration exceeds 0.4mol/dm<SUP>3</SUP>.
- 社団法人 粉体粉末冶金協会の論文
- 1999-04-15
著者
関連論文
- ゲータイトの結晶学的モルフォロジー制御
- オキシアルキルアミンを共存させた水酸化第1鉄の湿式酸化法による板状ゲータイト粒子の合成
- 磁気テープ材料の高機能化を指向した水溶液中で作製したゲータイト粒子の形状制御