メカニカルアロイングを利用したAl基アモルファス粉末のパルス通電焼結
スポンサーリンク
概要
- 論文の詳細を見る
In order to prepare a bulk amorphous alloy, Al-based amorphous powder was sintered. Mechanical alloyed Al<SUB>70</SUB>Ti<SUB>12</SUB>Si<SUB>18</SUB> powder was used. The powder structure included amorphous and nano-crystalline phases. This powder was milled with Sn, with lower melting point, by mechanical alloying for 36ks. The amorphous powder was coated with Sn by mechanical alloying. This milled powder was sintered by spark plasma sintering in the temperature over the melting point of Sn, but under the crystallization temperature of Al<SUB>70</SUB>Ti<SUB>12</SUB>Si<SUB>18</SUB> powder. A disk specimen of 10mm diameter and 2mm thickness was prepared. The disk specimen of the amorphous alloy was prepared at sintering temperature of 503K and holding time of 1.2ks at 375MPa. The specimen consisted of amorphous phase, crystallized phase and the remained Sn phase. The amorphous phase crystallized at sintering temperature of 533K.
- 1997-12-15
論文 | ランダム
- 高分子塗り床仕上げ材とその耐薬品性
- 高分子塗り床仕上げ材(耐薬品性高分子材料)
- Mercury(II) ion Potentiometric Sensor Based on a Sulfur Schiff's Base 1-(2-Hydroxy-1, 2-diphenylethylidene)thiosemicarbazide as Ionophore
- Novel Activity of TiO_2 for Catalytic Conversion of CO and H_2O to Alcohols in the Presence of K_2CO_3
- 公害防止・地域再生と都市計画 (大気汚染公害訴訟と被害者救済)