Microstructure Formation of Al/TiAl3 Composite Fabricated by Infiltration-combustion Synthesis (特集 多元系混合粉の焼結過程および焼結機構)
スポンサーリンク
概要
- 論文の詳細を見る
Infiltration-combustion reaction between Ti green compact and molten Al was studied. The infiltration height change obtained by in-situ measurement, showed a linear proportion to the root of immersing time, but an incubation period was observed in the initial stage of the immersion. Using thermocouple embedded in the Ti green compacts, the combustion temperature of Ti powder and molten Al was determined to be about 1360K, which is lower than the calculated adiabatic temperature, 1580K, of the combustion synthesis of TiAl<SUB>3</SUB>. In the preform immersed into molten Al for 30s, granular products were observed at the surfaces of Ti particles. By the observation on the helium-gas-quenched sample, it was confirmed that disintegrated Ti particles and spherical particles of TiAl<SUB>3</SUB> were formed. The crevice between the as-reacted TiAl<SUB>3</SUB> particles was found to be filled with molten Al by the further infiltration to form Al/TiAl<SUB>3</SUB> composite. The final microstructure of this reaction is a cermet type one with about 74 vol% of TiAl<SUB>3</SUB> and the average particle size is about 12μm.
- 社団法人 粉体粉末冶金協会の論文
- 1997-12-15
著者
-
Watanabe Ryuzo
Department Of Materials Processing Faculty Of Engineering Tohoku University
-
Watanabe Ryuzo
Department Of Material Processing Graduate School Of Engineering Tohoku University
-
Wang C‐m
National Inst. Res. In Inorganic Materials Ibaraki Jpn
-
WANG Chang-meng
Graduate School, Tohoku University
関連論文
- Heat Insulation Performance of Functionally Graded Metal/Ceramic Coatings and Fracture Behavior under High Heat Flux (特集 傾斜機能材料)
- Brittle-to Ductile Transition and High-Temperature Deformation in ZrO_2 (Y_2 O _3) and Al_2 O _3 Ceramics as Evaluated by Small Punch Test
- Microstructure and High-Temperature Property of Reaction HIP-Sintered SiC-AlN Ceramic Alloys
- Effects of Content and Size of Al2O3 Particle Dispersion on the Sintering Densification Rate of Y-PSZ/Al2O3 Composites (特集 多元系混合粉の焼結過程および焼結機構)
- Evaluation of High-Temperature Strength of Mo/PSZ Composites by Modified Small Punch Tests
- Effect of Microstructure on Thermal Shock Cracking of Functionally Graded Thermal Barrier Coatings Studied by Burner Heating Test
- Multi-Layered Potts Model Simulation of the Formation of Graded Structure in Iron-Copper Liquid-Phase-Sintered Alloy
- Thermoelectric Properties and Microstructure of(Zn_Al_)O Prepared by MA/HP Process
- Photostrictive Characteristics of Fine-Grained PLZT Ceramics Derived from Mechanically Alloyed Powder
- Breakaway Behavior of Surface Oxide Film on Aluminum-Sillicon-Magnesium Alloy Powder Particles at High Temperature in a Vaccuum
- Synthesis of Single Phase La_2Zr_2O_7 by Wet Mechanochemical Treatment
- Reaction Synthesis of Ti_3 SiC_2 from Mixture of Elemental Powders
- Multi-Layered Potts Model Simulation of Morphological Changes of the Neck during Sintering in Cu-Ni System
- Characterization of TiN-AlN Composites Prepared Through Mechanical Alloying and Followed by Pressure Sintering
- Synthesis and Microstructure of TiN-AIN Composite Powder by Mechanical Alloying
- Determination of Distribution Patterns of Fillers in Composites by Micromorphological Parameters
- Microstructural Dependence of Aging-Induced Phase Transformation in Y_2O_3-Partially-Stabilized ZrO_2 Polycrystals
- Microstructure and Mechanical Properties of TiB_2-W Cermets Prepared by HIP
- Preparation of A Thermoelectric Composite of AgSbTe_2/Ag_2Te by Mechanical Alloying
- Microstructure Formation of Al/TiAl3 Composite Fabricated by Infiltration-combustion Synthesis (特集 多元系混合粉の焼結過程および焼結機構)