ゲータイトの結晶学的モルフォロジー制御

スポンサーリンク

概要

• 論文の詳細を見る

• The crystallographical and morphological properties of goethite particles in the course of oxidation in the strong alkaline solution was studied from X-ray diffraction analysis under the systematically controlled synthesizing conditions. The crystallite size ratio, D<SUB>010</SUB>D<SUB>110</SUB>, was changed by excess alkali content and oxidation conditions. The particle morphology of goethite depends on the relative growth rates of each faces of goethite crystals. From the SEM observation, the vertical and horizontal axes of goethite are proposed to be (110) and the lateral growth is assumed to be occurred along (110) easily because of the topotaxy between Fe(OH)<SUB>2</SUB> and goethite. It is concluded that the crystallite size ratio depends on the development of (110) face during crystal growth, which in turn, is related to the ferrous complex (FeOH<SUP>+</SUP>) content.

• 社団法人 粉体粉末冶金協会の論文
• 1996-01-15

著者

• 浦井 智明

  戸田工業(株)

• 浦井 智明

  戸田工業

• 黒川 晴己

  戸田工業(株)創造本部

• 黒川 晴己

  戸田工業(株)小野田事業所事業開発グループ

関連論文

• 中空三次元構造を有するシングルナノ粒子の合成とディーゼルエンジン用NOx浄化用触媒への応用
• 中空3次元構造を有する複合酸化物のキャラクタリゼーション
• 中空三次元構造Ce複合酸化物微粒子の酸素吸蔵特性
• 磁気記録用酸化鉄の製造プロセス
• ゲータイトの結晶学的モルフォロジー制御
• オキシアルキルアミンを共存させた水酸化第1鉄の湿式酸化法による板状ゲータイト粒子の合成
• 磁気テープ材料の高機能化を指向した水溶液中で作製したゲータイト粒子の形状制御