メカニカルアロイング法のFeSi_2熱電材料への応用
スポンサーリンク
概要
- 論文の詳細を見る
The enhancement of thermoelectric properties of p-type β-FeSi<SUB>2</SUB> doped with Mn and Al by mechanical alloying (MA) was described. The pre-mixed powder of nominal composition Fe<SUB>30</SUB>Si<SUB>70</SUB> transforms to a homogeneous β-FeSi<SUB>2</SUB> phase in the as milled condition. The appropriate milling time of a powder for sintering was around 720 ks at which the powder consists of very fine Fe and Si crystals in the as milled condition. Specimens prepared by hot pressing from MA powder showed lower thermal conductivity, higher figure of merit and hence higher conversion efficiency than those prepared from ingot metallurgy. This was mostly due to the small grain size obtained by MA. Phase formation sequence in MA powder was discussed in conjunction with thin films. The formation sequence of β-FeSi<SUB>2</SUB> from the mixture of Fe and Si powders via ε-FeSi observed in MA powder and thin films of Fe with a Si substrate can be explained with the proposed two rules when the non-stable phases at room temperature were excluded. The possibility of the influence of MA energy on the phase formation sequence was also pointed out.
- 1995-02-15
論文 | ランダム
- C-34 遺伝性てんかんラット(IGER)脳のミクログリア動態について
- C-33 遺伝性てんかんラット(IGER)の海馬の微小神経形成異常の病理発生 : BrdUを用いた神経細胞の移動トレース実験
- 血小板由来増殖因子B鎖蛋白発現と関連した短いmRNAのクローニング
- 18. The metabolic syndromeにおける尿中コルチゾール代謝の検討(第54回近畿大学医学会学術講演会)
- 4. アンジオテンシン変換酵素阻害剤(ACE-I)とアンジオテンシンII受容体拮抗薬(ARB)による尿AVP量の変化(第53回近畿大学医学会学術講演会)